What is steel grade 1.8962?

     JAWAYSTEEL can produce 1.8962 stainless steel round rods, 1.8962 forging,sheet,coil,and profiled strip,Deformed steel,flat steel, mould,steel wire,have all specifications. With many years production experience, strict control 1.8962 chemical composition and 1.8962 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

Production specification
Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Length: We can supply any length based on the customer’s requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling +annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer’s requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer’s requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer’s requirement excellent service for all kinds of industries,with advantages of technologies, equipment and price.

Data Table for Steel Grades:1.8962
Mechanical properties of grade steel:1.8962
Chemical composition % of the ladle analysis of steel grade:1.8962


 C(%)

 Si(%)

Mn(%)

   P(%)

 S(%)

 Cr(%)

Max 0.12

0.25-0.75

0.20-0.50

Max 0.07-0.15

Max 0.035

0.50-1.25

Ni(%)

Mo(%)

 Ti(%)

V(%)

 W(%)

 Nb(%)

Max 0.65

 

 

   

 

 

Co(%)

  Cu(%)

  Al(%)

 B(%)

N(%)

  Other 

 

0.25-0.55

 

 

 

 

Technological properties of grade steel:1.8962
Hardness and heat treatment specification of steel grade:1.8962


Annealing hardness
HBS

Cold pull hardness
HBS

Preheating temperature

Quenching temperature

Holding time
min

Hardening medium

Temper temperature

After tempering hardness
≥HRC

salt-bath furnace

controlled atmosphere furnace

235

262

788

1191

1204

5~15

air cooling

522

60

Steel plate/Sheet
thickness / mm

σb
MPa

σs
≥/MPa

δ
Samples from the standard for 50 mm (2 in)

180 ° of cold bending test

longitudinal

horizontal

Hot-rolled/Cold rolling:5 - 150

520

415

16~18

2a

3.5a

Note:
(1) listed in the table apex diameter (d), to steel thickness (a) multiples said.
(2) in the ASTM A6 standard specified scope can meet any additional conditions.
(3) from the standard for 50 mm (2 in).

ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d’elasticite minimale
Rm Tensile strength / Zugfestigkeit / Resistance a la traction
A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal
J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc