Austenitic:

Type 301 contains less chromium and nickel than 302 for more work hardening.

Type 302 is the basic type of the 300 series, 18% chromium— 8% nickel group. It is the renowned 188

Stainless and is the most widely used of the chromium nickel stainless and heat resisting steels.

Type 303 contains added phosphorus and sulfur for better machining characteristics.Corrosion resistance is slightly less than 302/304.

Type 303Se contains Se and P added to improve machinability.

Type 305 has increased nickel to lower work hardening properties.

Type 309309Shave added chromium and nickel for more corrosion resistance and high temperature scaling resistance. 309S contains less carbon to minimize carbide precipitation.

Type 310310Shave higher nickel content than 309309Sto further increase scaling resistance.310S contains less carbon than 310 to minimize carbide precipitation.

Type 321 contains titanium to tie up the carbon and avoid chromium carbide precipitation in welding.

Type 330 ultra high nickel content provides best corrosion resistance to most furnace atmospheres. This grade has low coefficient of expansion, excellent ductility and high strength.

Type 347 – 348 have columbium tantalum added to tie up the carbon and avoid chromium carbide precipitation in welding. Use for temperatures from 800to 1650 degrees F.

 

Ferritic:

 

Type 405 contains 12% chromium with aluminum added to prevent hardening.

Type 430 is the basic type in the ferritic group, possessing good ductility and excellent resistance to atmospheric corrosion. Its scaling resistance is higher than 302 in intermittent service, somewhat lower in continuous use.

Type 430F430Sehave sulfur and selenium (respectively) added for increased machinability.

Type 442 has added chromium for improved resistance to scaling.

Type 446 has still higher chromium content (27%) for added scaling resistance and is highest of the standard straight chromium types. Alloys with over 30% chromium become too brittle to process.